Tensile strength of glass fibres with carbon nanotube–epoxy nanocomposite coating: Effects of CNT morphology and dispersion state — Naveed A. Siddiqui (2010) | RDL Network
Back
Cite
Save
Save for later
Share
Home
Publications
Tensile strength of glass fibres with carbon nanotube–epoxy nanocomposite coating: Effects of CNT morphology and dispersion state
BT
Shared by
Ben Zhong Tang
Tensile strength of glass fibres with carbon nanotube–epoxy nanocomposite coating: Effects of CNT morphology and dispersion state
Article
2010
en
Authors
+4 more
NS
Naveed A. Siddiqui
EL
Erin L. Li
MS
Man‐Lung Sham
Discussion
(0)
Sign in
to like and join the discussion.
No comments yet. Be the first to comment.
Related publications
Article
2009
Tensile strength of glass fibres with carbon nanotube–epoxy nanocomposite coating
Naveed A. Siddiqui
,
Man‐Lung Sham
,
Ben Zhong Tang
,
Arshad Munir
,
Jang‐Kyo Kim
Article
2007
Carbon Nanotube Dispersion and Functionalization for Nanocomposite Manufacturing
Peng‐Cheng Ma
,
Ben Zhong Tang
,
Jang‐Kyo Kim
Article
2018
Strength and failure mechanisms of cnt-reinforced copper nanocomposite
Bruno Faria
,
Cátia Guarda
,
Nuno Silvestre
,
José N. Canongia Lopes
,
Diogo Galhofo
Composites Part B Engineering
Article
2016
Copper oxide-carbon nanotube (CuO/CNT) nanocomposite: Synthesis and photocatalytic dye degradation from colored textile wastewater
Niyaz Mohammad Mahmoodi
,
Pardis Rezaei
,
Cyrus Ghotbei
,
Mohammad Kazemeini
Fibers and Polymers
Article
2007
Effects of silane functionalization on the properties of carbon nanotube/epoxy nanocomposites
Peng‐Cheng Ma
,
Jang‐Kyo Kim
,
Ben Zhong Tang
Discussion(0)
No comments yet. Be the first to comment.