SYNTHESES TiO2 NANOCOMPOSITE USING EVAPORATION-INDUCED SELF-ASSEMBLY (EISA) METHOD FOR DSSC

The objective of this study is to synthesize mesoporous titania using the EvaporationInduced Self-Assembly (EISA) method. The samples were annealled at 400 ° C for 4 hours. Then the titania was pasted onto FTO glass and immersed in dye N719 for several hours. TiO2 using EISA method and time immersing in the dye were prepared for comparison. Titanium Tetra Isopropoxide (Ti(OiPr4)) was chosen as a precursor and Trymethil Ammonium Bromide (CTAB) as a surfactant. From SEM results, TiO2 EISA produced small TiO2 particles with high porosity and compact particles. From XRD spectrum, anatase phase had been produced by using this EISA method. Percentage efficiency for TiO2 EISA that being immersed in the dye for 12 hours, and 6 hours is about 2.81% and 2.24%, respectively. The results show that TiO2 gave a good result in terms of efficiency and will lead to a better DSSC system.