A series of Beta zeolites have been synthesized in the presence of tetraethylammonium hydroxide (TEA). Samples with Si/Al ratio in the 7-100 range have been characterized by X-ray powder diffraction, I.R. spectroscopy, and pyridine adsorption. The fraction of TEA which is compensating the charge of the framework aluminum is removed at temperatures higher than those required to remove "occluded" TEA. Three hydroxyl bands are observed at 3740 cm-1 (silanol groups), 3680 cm-1 (extraframework Al) and 3615 cm-1 (acid hydroxyl groups interacting with pyridine). Comparison of the catalytic properties of H-Beta and H-Y zeolites for cracking n-heptane and gasoil shows that zeolite Beta should have more than one type of channel with different dimensions. For gas-oil cracking, zeolite Beta is less active and produces more coke and less gasoline than zeolite HY.