Tensile crack tip fields in elastic-ideally plastic crystals

Crack tip stress and deformation fields are analyzed for tensile-loaded ideally plastic crystals. The specific cases of (0 1 0) cracks growing in the [1 0 1] direction, and (1 0 1) cracks in the [0, 1, 0] direction, are considered for both fcc and bcc crystals which flow according to the critical resolved shear stress criterion. Stationary and quasistatically growing crack fields are considered. The analysis is asymptotic in character; complete elastic-plastic solutions have not been determined. The near-tip stress state is shown to be locally constant within angular sectors that are stressed to yield levels at a stationary crack tip, and to change discontinuously from sector to sector. Near tip deformations are not uniquely determined but fields involving shear displacement discontinuities at sector boundaries are required by the derived stress state. For the growing crack both stress and displacement must be fully continuous near the tip. An asymptotic solution is given that involves angular sectors at the tip that elastically unload from, and then reload to, a plastic state. The associated near-tip velocity field then has discontinuities of slip type at borders of the elastic sectors. The rays, emanating from the crack tip, on which discontinuities occur in the two types of solutions are found to lie either parallel or perpendicular to the family of slip plane traces that are stressed to yield levels by the local stresses. In the latter case the mode of concentrated shear along a ray of discontinuity is of kink type. Some consequences of this are discussed in terms of the dislocation generation and motion necessary to allow the flow predicted macroscopically.