Selective Laser Melting process optimization of Ti–Mo–TiC metal matrix composites

Selective Laser Melting (SLM) was used to process a powder mixture of CP Ti, 6.5 wt% Mo and 3.5 wt% Mo2C. The process parameters were optimized to obtain full-density, crack free parts. After the in situ decomposition of Mo2C in favor of the formation of TiC, the material consisted of a homogeneous dispersion of submicrometer sized TiC platelets in a β-(Ti,Mo) matrix exhibiting a high hardness up to 550 HV and compressive yield stress of 1164 ± 37 MPa. The microstructure and mechanical properties could be tailored by variation of the process parameters within the high-density processing window, as well as through post-process heat treatments.