Scanning Kelvin probe force microscopy as a means of predicting the electrochemical characteristics of the surface of a modified AA4xxx/AA3xxx (Al alloys) brazing sheet

Macro- and micro-electrochemical properties of clad and core surfaces of a modified AA4xxx/AA3xxx brazing sheet material, before and after brazing, have been evaluated and compared. By scanning Kelvin probe force microscopy (SKPFM), the Volta potential distribution over the brazed and non-brazed clad surfaces was measured. The changes in the Volta potential maps were correlated to the macro-electrochemical responses of the surfaces and the microstructural features that evolve as a result of brazing. By performing potentiodynamic polarization experiments and microscopic analysis of the corroded surfaces and cross sections, the suitability of SKPFM analysis for corrosion performance prediction of the aluminium brazing sheet material in a sea water acidified accelerated test (SWAAT) environment was confirmed. Considering the purity of Si phase in the structures of both brazed and non-brazed material, it is suggested that Si can be applied as a reliable local reference in both structures to compare the changes in Volta potential differences as the result of different heat treatments of aluminium brazing sheet. Increasing the copper content of the re-solidified clad material as a result of brazing treatment was found to increase the Volta potential of the matrix which in turn reduces the cathodic protection power of the re-solidified clad material towards the core material.