Mechanical and Tribological Performance of Additively Manufactured Nanocrystalline Aluminum via Cryomilling and Cold Spray

In this study, nanocrystalline (NC) aluminum (Al) and magnesium (Mg)-doped Al bulk components were fabricated using a hybrid manufacturing process that combines cryomilling and high-pressure cold spray (HPCS) additive deposition techniques. Yttria-stabilized zirconia (YSZ) was also added during the HPCS process to improve deposition efficiency and build-up thickness via peening. The evolution of morphology, crystallite size, and elemental composition of both cryomilled powders and cold-sprayed (CS’ed) components was systematically characterized using X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM). Mechanical characterization was performed using Vickers microhardness and uniaxial tensile testing, while the tribological behavior was assessed using sliding wear tests under dry/lubricated conditions. XRD analysis revealed that increased cryomilling duration led to significant crystallite refinement, which directly correlated with enhanced hardness and strength. This mechanical strengthening was accompanied by an increase in coefficient of friction (COF) and lower wear rates. The results also showed that the Mg-doped Al exhibited superior hardness, tensile strength, and tribological performance compared to pure Al. The study further explores the underlying mechanisms responsible for these enhancements, highlighting the potential of solute-assisted grain boundary stabilization in tailoring high-performance NC Al alloys.