Influence of Metal Compounds on Structural and Electrochemical Characteristics of Chars from PVC Pyrolysis

This study aims to investigate the influence of various metal compounds (ZnO, ZnCl2, Zn(OH)2, MgO, MgCl2, and Mg(OH)2) on the structural and electrochemical properties of chars derived from the pyrolysis of polyvinyl chloride (PVC). Raw PVC samples mixed with different metal compounds were firstly pyrolyzed at 500 °C in a fixed-bed reactor. The produced chars were further pyrolyzed at 800 °C. The objective was to evaluate the impact of these metal compounds on the char structure through comparative analysis. The pyrolytic chars were characterized using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Raman spectroscopy, and Brunauer–Emmett–Teller (BET) analysis. Zinc-based additives notably increased carbon yield to 32–34 wt.%, attributed to ZnCl2-induced cross-linking. Specifically, ZnO facilitated porous architectures and aromatic structures with six or more rings. Mg-based compounds induce the formation of a highly stacked carbon structure primarily composed of crosslinked cyclic alkenes, rather than large polyaromatic domains. Upon further thermal treatment, these aliphatic-rich stacked structures can be progressively transformed into aromatic frameworks through dehydrogenation reactions at elevated temperatures. A high-surface-area porous carbon material (PVC/ZnO-800, SSA = 609.382 m2 g−1) was synthesized, demonstrating a specific capacitance of 306 F g−1 at 1 A g−1 current density.