Incorporating geranium plant waste into ultra-high performance concrete prepared with crumb rubber as fine aggregate in the presence of polypropylene fibers

Abstract This research examines the efficiency of ultra-high-performance concrete (UHPC) when utilizing geranium plant (GP) ash, which is subjected to different curing temperatures ranging from 300 to 900°C for 3 h of burning time. The GP ash is used as a replacement for cement in varying amounts (10, 20, 30, 40, and 50 wt%). Crumb rubber powder is utilized as a substitute for fine aggregate. Polypropylene fibers have been used to improve concrete performance. The performance of UHPC is evaluated by assessing its mechanical qualities, such as flexural strength, splitting tensile strength, and compressive strength. The sorptivity test is also evaluated as a component of it. Scanning electron microscopy is used to analyze UHPC after exposure to temperatures as high as 900°C. The findings demonstrated a notable enhancement in the mechanical characteristics of all mixtures. The most favorable mixtures were achieved with proportions of 50, 40, 40, and 20% for mixtures including GP waste incinerated at temperatures ranging from 300 to 900°C. Furthermore, the optimal outcome is achieved when 40% substitution is performed at a temperature of 700°C, resulting in notable enhancements of 14% in compressive strength, 30% in flexural strength, and 17% splitting tensile strength, respectively. At a high temperature of 700°C, the decrease in strength increased to approximately 37–40% as a result of the initial removal of carbon dioxide from calcite at temperatures ranging from 600 to 900°C and reached 56% at 900°C. Great resistance to sorptivity, as well as a dense and compact microstructure with a high content of calcium and silicon, was obtained.