Environmental degradation of thermal-barrier coatings by molten deposits

Carlos G. Levi; John W. Hutchinson; M.H. Vidal-Sétif; C. A. Johnson

doi:10.1557/mrs.2012.230

Environmental degradation of thermal-barrier coatings by molten deposits

MRS Bulletin 37(10): 932-941

Article 2012 English

Abstract

1 min read

Molten deposits based on calcium-magnesium alumino-silicates (CMAS), originating from siliceous debris ingested with the intake air, represent a fundamenta

Related publications

Article2008

Mechanisms of cracking and delamination within thick thermal barrier systems in aero-engines subject to calcium-magnesium-alumino-silicate (CMAS) penetration

Stephan Krämer, S. Faulhaber, M.D. Chambers, David R. Clarke, Carlos G. Levi, John W. Hutchinson, A.G. Evans

Materials Science and Engineering A

Article2009

Delamination Susceptibility of Coatings Under High Thermal Flux

Zhiming Xue, A.G. Evans, John W. Hutchinson

Journal of Applied Mechanics

Preprint2014

Internal structure of event layers preserved on the Andaman Sea continental shelf, Thailand: tsunami vs. storm and flash flood deposits

D. Sakuna-Schwartz, Peter Feldens, Klaus Schwarzer, Somkiat Khokiattiwong, Karl Stattegger

Article2016

Currentless Deposition of Niobium-Based Protective Coatings for Application in Molten Salts

А. В. Абрамов, Ilya B. Polovov, Vladimir A. Volkovich, Oleg I. Rebrin

ECS Transactions

Article2015

Internal structure of event layers preserved on the Andaman Sea continental shelf, Thailand: tsunami vs. storm and flash-flood deposits

D. Sakuna-Schwartz, Peter Feldens, Klaus Schwarzer, Somkiat Khokiattiwong, Karl Stattegger

Natural hazards and earth system sciences

Environmental degradation of thermal-barrier coatings by molten deposits

Abstract

Discussion(0)

Related publications

Mechanisms of cracking and delamination within thick thermal barrier systems in aero-engines subject to calcium-magnesium-alumino-silicate (CMAS) penetration

Delamination Susceptibility of Coatings Under High Thermal Flux

Internal structure of event layers preserved on the Andaman Sea continental shelf, Thailand: tsunami vs. storm and flash flood deposits

Currentless Deposition of Niobium-Based Protective Coatings for Application in Molten Salts

Internal structure of event layers preserved on the Andaman Sea continental shelf, Thailand: tsunami vs. storm and flash-flood deposits