A coupled environment model for stress corrosion cracking in sensitized type 304 stainless steel in LWR environments — Digby D Macdonald (1991) | RDL Network
Back
Cite
Save
Save for later
Share
Home
Publications
A coupled environment model for stress corrosion cracking in sensitized type 304 stainless steel in LWR environments
Shared by
Digby D Macdonald
University of California, Berkeley
A coupled environment model for stress corrosion cracking in sensitized type 304 stainless steel in LWR environments
Article
1991
en
Authors
Digby D Macdonald
University of California, Berkeley
MU
Mirna Urquidi‐Macdonald
Discussion
(0)
Sign in
to like and join the discussion.
No comments yet. Be the first to comment.
Related publications
Article
2005
Stress corrosion cracking of sensitized Type 304 stainless steel in thiosulphate solution. II. Dynamics of fracture
Monika Gomez-Duran
,
Digby D Macdonald
Article
2003
Stress corrosion cracking of sensitized Type 304 stainless steel in thiosulfate solution: I. Fate of the coupling current
Monika Gomez-Duran
,
Digby D Macdonald
Article
1985
Stress Corrosion Cracking of Sensitized AISI 304 Stainless Steel in Oxygenated High Temperature Chloride Solutions Containing Cupric (Cu2+) and Lead (Ph2+) Ions
Digby D Macdonald
,
A. K. Eghan
,
Z. Szklarska‐Śmiałowska
Article
2014
Prediction of crack growth rate in Type 304 stainless steel using artificial neural networks and the coupled environment fracture model
Jiangbo Shi
,
Jihui Wang
,
Digby D Macdonald
Article
2018
Customization of the coupled environment fracture model for predicting stress corrosion cracking in Alloy 600 in PWR environment
Jiangbo Shi
,
Balázs Fekete
,
Jihui Wang
,
Digby D Macdonald
.webp){kind=small}
Discussion(0)
No comments yet. Be the first to comment.